Tin Oxide Nanoparticles: Synthesis, Characterization and Study their Particle Size at Different Current Density

  • Karzan A. Omar Department of Chemistry, University of Dr. Babasaheb Ambedkar Marathwada.
Keywords: Band gap, Electrochemical cell, Tetrabutylammonium bromide (TBAB), Tetrapropylammonium bromide (TPAB), Tin oxide nanoparticles.

Abstract

Tin oxide nanoparticles are prepared by electrochemical reduction method using tetrapropylammonium bromide (TPAB) and tetrabutylammonium bromide (TBAB) as structure directing agent in an organic medium viz. tetrahydrofuran (THF) and acetonitrile (ACN) in 4:1 ratio by optimizing current density and molar concentration of the ligand. The reduction process takes place under an inert atmosphere of nitrogen over a period of 2 h. Such nanoparticles are prepared by using a simple electrolysis cell in which the sacrificial anode as a commercially available in tin metal sheet and platinum (inert) sheet act as a cathode. The parameters such as current density, solvent polarity, distance between electrodes and concentration of stabilizers are used to control the size of nanoparticles. The synthesized tin oxide nanoparticles are characterized by using UV–Visible, FT-IR and SEM–EDS analysis techniques. UV-Visible spectroscopy has revealed the optical band gap to be 4.13, 4.16 and 4.24 ev for (8, 10 and 12 mA/cm2) and the effect of current density on theirs particle size, respectively.

Downloads

Download data is not yet available.

Author Biography

Karzan A. Omar, Department of Chemistry, University of Dr. Babasaheb Ambedkar Marathwada.
Department of Chemistry

References

Kim, T.W., Lee, D.U., Choo, D.C., Kim, J. H., Kim, H. J., Jeong, J. H., Jung,

M., Bahang, J.H., Park, H.L., Yoon, Y.S. and Kim, J.Y., 2002. Optical parameters in SnO2 nanocrystalline textured films grown on p-lnSb (111) substrates, J. Phys. Chem. Solids, 63, pp.881-885.

Moustafid, T.E., Cachet, H., Tribollet, B., and Festy, D., 2002. Modified transparent SnO2 electrodes as efficient and stable cathodes for oxygen reduction, Electrochimica Acta, 47(8), pp.1209–1215.

Okuya, M., Kaneko, S., Hiroshima, K., Yaggi, I. and Murakami, K., 2001. Low Temperature Deposition of SnO2 Thin Films as Transparent Electrodes by Spray Pyrolysis of Tetra-n-butyltin(IV), J. Eur. Ceram. Soc., 21, pp.2099-2102.

Chen, F.L. and Liu, M.L., 1999. Preparation of mesoporous tin oxide for electrochemical applications, Chem. Commun., 8, 1829-1830.

Kim, C., Noh, M., Choi, M., Cho, J. and Park, B., 2005. Critical size of a nano SnO2 electrode for Li-secondary battery. Chem Mater, 17(12), pp.3297–3301.

Chou, L., Cai, Y., Zhang, B., Niu, J., Ji, S. and Li, S., 2003. Influence of SnO2-doped W-Mn/SiO2 for oxidative conversion of methane to high hydrocarbons at elevated pressure, Appl. Catal. A Gen., 238, pp.185-191.

Wierzchowski, P.T. and Zatorski, L. W., 2003. Kinetics of catalytic oxidation of carbon monoxide and methane combustion over alumina supported Ga2O3, SnO2 or V2O5, Appl. Catal. B Environ., 44, pp.53-65.

Moulson, A. J. and Herbert, J.M. 1990. Electroceramics, Chapman & Hall, New York.

Li, G.J., Zhang, X.H. and Kawi, S., 1999. Relationships between sensitivity, catalytic activity and surface areas of SnO2 gas sensors. Sens. Actuators B, 60, pp.64-70.

Sharp, S.L., Kumar, G., Vicenzi, E.P. and Bocarsly, A.B., 1998. Formation and Structure of a Tin-Iron Oxide Solid-State with Petential Applications in Carbon Monoxide Sensing through the Use of Cyanogel Chemistry. Chemistry of Materials, 10, pp.880-885.

Farrukh, M.A. and Heng, B.-T. and Adnan, R., 2010., Surfactant-controlled aqueous synthesis of SnO2 nanoparticles via the hydrothermal and conventional heating methods, Turkish Journal of Chemistry, 34(4), pp.537-550.

Published
2013-11-20
How to Cite
Omar, K. A. (2013) “Tin Oxide Nanoparticles: Synthesis, Characterization and Study their Particle Size at Different Current Density”, ARO-THE SCIENTIFIC JOURNAL OF KOYA UNIVERSITY, 1(1), pp. 17-21. doi: 10.14500/aro.10028.
Section
Articles