Experimental Assessment and Prediction of Physical Properties of Nanosilica-Modified Asphalt Cement

Abstract

Modifying the asphalt binder is one technique for improving asphalt pavement performance. When nanoparticles are utilized to modify asphalt binders, they exhibit unique and significant properties. Without a doubt, silica is the most commonly added element as nanoparticles to asphalts. The main objective of this study was to investigate the effect of mixing speed used to produce nanosilica (NS)-modified-asphalt cement on conventional physical properties of asphalt cement and prepare a model to predict the physical properties of NS-modified asphalt cement. For this purpose, four different nanosilica contents (1.5%, 3%, 4.5%, and 6% of the asphalt cement weight) were utilized. Each content was mixed at a temperature of 160°C using a high shear mixer set to four different speeds (1,000 rpm, 2,000 rpm, 3,000 rpm, and 4,000 rpm) for 30 min. Conventional asphalt cement tests, including penetration, softening point, rotational viscosity, and ductility tests, are conducted to evaluate the nanosilica-modified asphalt cement properties. The results showed that higher NS contents improve the physical properties of modified asphalt cement, but the improvement is more noticeable when mixing at a faster speed, as this lowers penetration and rotational viscosity and raises the softening point. By utilizing the Minitab statistical program, the physical properties prediction models of the NSmodified asphalt showed a direct correlation between input data (NS content, NS average size, mixing temperature, mixing rotational speed, mixing time, and neat asphalt properties) and predictive models, demonstrated by a high R2 value and acceptable standard deviation values.